Film-faced plywood is the most popular plywood produced by manufacturers in Vietnam. There are 5 common defects of film faced plywood by Vietnam manufacturers:To get more news about commercial plywood, you can visit boosterplywood.com official website.

Burn film is the most popular defect of film-faced plywood. Burn film is the film integrity damage caused by internal or external defects.

2/ LOCAL BUBBLES ON FILM FACED PLYWOOD SURFACE
Local bubbles on the plywood surface are caused by glue line delamination, which appears local bulges on the plywood surface.
3/ EDGE CHIPS ON FILM FACED PLYWOOD
Edge chips constitute the defect characterized by the lack of laminating film on the edges of a plywood sheet.

4/ LOCAL LAMINATION OF FILM FACED PLYWOOD SHEETS
Lamination is the splitting of two adjacent veneer layers along with the glue layer. And this makes the plywood weak and it’s not acceptable for a finished plywood.
5/ FILM POWDERING
Film powdering is the breaking of the laminating film away from the underlying plywood base along the edges. It’s caused by the worker’s mistake when put the film into the face before the hot-press process.
However, these pre-finished solution does not completely prevent the plywood from the defect as many parts of the manufacturing process is participated by humans. To ensure quality, after manufacturing inspection is utterly important. With many years of manufacturing experience and a deep understanding of plywood, FOMEX Group ensures not only input, manufacturing process but also the finished goods. We establish a professional Quality Control Team to inspect meticulously every piece of Plywood, do the testing and make a report for all consignments before on board.